Honeycomb structure and assembly thereof

ABSTRACT

A honeycomb structure obtained by bonding, into one piece, a plurality of honeycomb segments ( 2 ) each having a large number of passages ( 6 ) surrounded by cell walls and extending in the axial direction of the segment. In the honeycomb structure, a material A ( 3 ) having compressive elasticity ( 3 ) is provided at least at a portion of the gaps formed by each two faces of adjacent honeycomb segments ( 2 ), close to each other. A honeycomb structure assembly ( 8 ) obtained by providing a material B ( 5 ) having compressive elasticity on the outer peripheral portion of the above honeycomb structure in a compressed state and thereby compression-holding the honeycomb structure in a metallic container ( 11 ). The honeycomb structure and the honeycomb structure assembly have good durability to a heat or a vibration, applied during their use.

TECHNICAL FIELD

[0001] The present invention relates to a honeycomb structure used in, for example, a carrier for a catalyst having a catalytic action, for use in internal combustion engine, boiler, chemical reactor, fuel cell reformer, etc. and a filter for trapping fine particles present in an exhaust gas; as well as to an assembly thereof. More particularly, the present invention relates to a honeycomb structure which hardly breaks when exposed to a vibration or a thermal stress during its use, as well as to an assembly thereof.

BACKGROUND ART

[0002] Honeycomb structures are in use in, for example, a carrier for a catalyst having a catalytic action, for use in internal combustion engine, boiler, chemical reactor, fuel cell reformer, etc. and a filter for trapping fine particles present in an exhaust gas, particularly fine particles emitted from a diesel engine.

[0003] In the honeycomb structure used for such a purpose, the sharp temperature change of exhaust gas and the local heating makes non-uniform the temperature distribution inside the honeycomb structure and there have been problems such as crack generation in honeycomb structure and the like. When the honeycomb structure is used particularly as a filter for trapping a particulate substance in an exhaust gas emitted from a diesel engine, it is necessary to burn the fine carbon particles deposited on the filter to remove the particles and regenerate the filter and, in that case, high temperatures are inevitably generated locally in the filter; as a result, a large thermal stress and cracks have tended to generate.

[0004] Hence, there were proposed processes for producing a honeycomb structure by bonding a plurality of individual honeycomb segments using an adhesive. In, for example, U.S. Pat. No. 4,335,783 is disclosed a process for producing a honeycomb structure, which comprises bonding a large number of honeycomb parts using a discontinuous adhesive. Also in JP-B-61-51240 is proposed a thermal shock-resistant rotary regenerating heat exchanging method which comprises forming, by extrusion, matrix segments of honeycomb structure made of a ceramic material, firing them, making smooth, by processing, the outer peripheral portions of the fired segments, coating the to-be-bonded areas of the resulting segments with a ceramic adhesive having, when fired, substantially the same chemical composition as the matrix segments and showing a difference in thermal expansion coefficient, of 0.1% or less at 800° C., and firing the coated segments. Also in a SAE article 860008 of 1986 is disclosed a ceramic honeycomb structure obtained by bonding cordierite honeycomb segments with a cordierite cement. Further in JP-A-8-28246 is disclosed a ceramic honeycomb structure obtained by bonding honeycomb ceramic members with an elastic sealant made of at least a three-dimensionally intertwined inorganic fiber, an inorganic binder, an organic binder and inorganic particles.

[0005] Meanwhile, the regulation for exhaust gas has become stricter and engines have come to have higher performances. As a result, in order to achieve an improvement in combustion conditions of engine and an increase in purification ability of catalyst, the temperature of exhaust gas has increased year by year. In this connection, a higher thermal shock resistance and a higher vibration resistance have come to be required for honeycomb substrate. Therefore, even with honeycomb structures such as mentioned above, when the vibration, heat, exhaust gas pressure, etc. applied thereto during their use are larger, it is possible that cracks, etc, appear in the adhesive used therein or the areas bonded therewith and, in an extreme case, there occur, for example, the disintegration of honeycomb structure and the breakage of the structure into fine pieces caused by vibration.

[0006] The present invention has been made in view of the above situation. It aims at providing a honeycomb structure which is further improved in durability to the vibration, heat, exhaust gas pressure, etc. applied during the use, and an assembly thereof.

DISCLOSURE OF THE PRESENT INVENTION

[0007] The first invention provides a honeycomb structure obtained by bonding, into one piece, a plurality of honeycomb segments each having a large number of passages surrounded by cell walls and extending in the axial direction of the segment, characterized in that a material A having compressive elasticity is provided at least at a portion of the gaps formed by each two faces of adjacent honeycomb segments, close to each other.

[0008] In the first invention, it is preferable that the material A having compressive elasticity is a ceramic fiber-made mat, and it is further preferable that the ceramic fiber-made mat is a non-intumescent mat composed mainly of alumina or mullite. It is also preferable that the honeycomb structure of the first invention is used for purification of exhaust gas of automobile, and it is further preferable that the honeycomb structure is used as a filter for trapping diesel fine particles. In the first invention, it is also preferable that the main component of the honeycomb segment comprises at least one kind of ceramic selected from the group consisting of silicon carbide, silicon nitride, cordierite, alumina, mullite, zirconia, zirconium phosphate, aluminum titanate, titania, combinations thereof, a Fe—Cr—Al type metal, a nickel-based metal, or metallic Si and SiC.

[0009] The second invention provides a honeycomb structure assembly obtained by providing a material B having compressive elasticity, on the outer peripheral portion of the above honeycomb structure in a compressed state and thereby compression-holding the honeycomb structure in a metallic container.

[0010] In the second invention, the material B having compressive elasticity is preferably a ceramic fiber-made mat, further preferably a heat-intumescent mat containing vermiculite, more preferably a non-intumescent mat composed mainly of alumina or mullite. The honeycomb structure assembly is preferably obtained by canning by a stuffing method, a tourniquet method, a clamshell method or a swaging method. Further, the honeycomb structure assembly is preferably obtained by loading a catalyst on honeycomb segments and then accommodating the catalyst-loaded honeycomb segments in a metallic container. Also, the honeycomb structure assembly is preferably obtained by accommodating honeycomb segments in a metallic container and then loading a catalyst on the honeycomb segments.

BRIEF DESCRIPTION OF THE DRAWINGS

[0011]FIG. 1 is a schematic top view showing one embodiment of the honeycomb structure of the present invention.

[0012]FIG. 2 is a schematic top view showing one embodiment of the honeycomb structure assembly of the present invention.

[0013]FIG. 3 is a partially cut-away view showing one example of the stuffing method used for stuffing a honeycomb structure in a metallic container.

[0014]FIG. 4 is a perspective view showing one example of the tourniquet method used for accommodating a honeycomb structure in a metallic container.

[0015]FIG. 5 is a perspective view showing one example of the clamshell method used for accommodating a honeycomb structure in a metallic container.

[0016]FIG. 6 is a sectional view parallel to the direction of passage, showing one example of the swaging method used for accommodating a honeycomb structure in a metallic container.

[0017]FIG. 7 is a sectional view parallel to the direction of passages, showing one example of the swaging method used for accommodating a honeycomb structure in a metallic container.

[0018] FIGS. 8(a), 8(b) and 8(c) are each a schematic top view of the honeycomb structure produced in Example. FIG. 8(a) shows the honeycomb structure of Example 1; FIG. 8(b) shows the honeycomb structure of Example 2; and FIG. 8(c) shows the honeycomb structure of Example 3.

[0019] FIGS. 9(a) and 9(b) are each a schematic top view of the honeycomb structure produced in Comparative Example. FIG. 9(a) shows the honeycomb structure of Comparative Example 1; and FIG. 9(b) shows the honeycomb structure of Comparative Example 2.

[0020]FIG. 10 is a graph showing the result of a hot vibration test.

BEST MODE FOR CARRYING OUT THE INVENTION

[0021] The honeycomb structure and honeycomb structure assembly of the present invention are described in detail below with reference to the accompanying drawings. However, the present invention is not restricted to the following mode. Incidentally, in the following, “section” refers to a section vertical to the direction of passage unless otherwise specified.

[0022]FIG. 1 is a schematic top view showing one embodiment of the honeycomb structure of the present invention. The honeycomb structure 1 of the present invention shown in FIG. 1 is constituted by providing, as a material A having compressive elasticity, a ceramic fiber-made mat 3 at the gaps formed by each two close faces of two adjacent honeycomb segments 2 each having a large number of passages 6 surrounded by cell walls and extending in the axial direction of the segment.

[0023] The characteristic constitution of the present invention is that a material A having compressive elasticity is provided at least at a portion of the gaps formed by each two faces of adjacent honeycomb segments 2, close to each other. Employing such a constitution, the honeycomb structure of the present invention is improved in durability to the vibration, heat, exhaust gas pressure, etc. applied during the use. In the present invention, “providing a material A having compressive elasticity at least at a portion of the gaps formed by each two close faces” means that it is sufficient to provide the material A having compressive elasticity at a portion of part of the gaps formed by each two close faces. However, it is preferred that the material A having compressive elasticity is provided at the whole portion of part of the gaps or at a portion of the gaps, and it is further preferred that the material A having compressive elasticity is provided at the whole portion of the gaps.

[0024] In the present invention, the material A having compressive elasticity is preferred to have heat resistance and cushioning. As the compressive elasticity material A having heat resistance and cushioning, there is a non-intumescent material containing substantially no vermiculite or a low-intumescent material containing a small amount of vermiculite. Such a material is preferred to contain, as a main component, a ceramic fiber made of at least one kind selected from the group consisting of alumina, high alumina, mullite, silicon carbide, silicon nitride, zirconia and titania, or of a composite thereof. Of these, a non-intumescent material containing substantially no vermiculite and composed mainly of alumina or mullite is more preferred. Further, the material A having compressive elasticity is preferred to be a mat made of such a fiber, and the ceramic fiber-made mat is preferred to be a non-intumescent mat composed mainly of alumina or mullite. Further preferably, these ceramic-made mats have a sealing property for preventing the leakage of to-be-treated fluid. Preferred specific examples of the material A having compressive elasticity are 1100HT produced by 3M Co. and Maftec produced by Mitsubishi Chemical Corporation.

[0025] In the present invention, it is preferred that the material A having compressive elasticity is provided at the whole portion of the gaps formed by each two close faces of adjacent honeycomb segments 2. However, when the material A having compressive elasticity is provided only at selected gaps, an adhesive may be used for bonding, at other gaps not provided with the material A having compressive elasticity.

[0026] In the present invention, each honeycomb segment 2 is preferred to contain, as a main component, at least one kind of ceramic selected from the group consisting of silicon carbide, silicon nitride, cordierite, alumina, mullite, zirconia, zirconium phosphate, aluminum titanate, titania and combinations thereof, a Fe—Cr—Al type metal, a nickel-based metal, or metallic Si and SiC, from the standpoints of the strength, heat resistance, etc. of the honeycomb segment. In the present invention, “main component” means a substance which is 80% by mass or more of all components and which becomes a main crystalline phase.

[0027] The cell density of the honeycomb segment 2 is preferably 0.9 to 310 cells/cm² (6 to 2,000 cells/in.²). When the cell density is less than 0.9 cell/cm², the geometric surface area is insufficient. When the cell density is more than 310 cells/cm², the pressure loss is too large. The sectional shape (cell shape) of the passage of the honeycomb segment 2 is preferably any of a triangle, a tetragon and a hexagon from the standpoint of production of honeycomb segment.

[0028] The section of the honeycomb segment 2 has at least one side of preferably 30 mm or more, more preferably 50 mm or more, most preferably 70 mm or more from the standpoint of providing the material A having compressive elasticity in production of the honeycomb segment.

[0029]FIG. 2 is a schematic top view of a honeycomb structure assembly 8 obtained by holding a honeycomb structure shown in FIG. 1, in a metallic container 11. The honeycomb structure assembly 8 of the present invention, shown in FIG. 2 is obtained by providing a material B having compressive elasticity, on the outer peripheral portion of a honeycomb structure 1 in a compressed state and thereby compression-holding the honeycomb structure 1 in a metallic container 11.

[0030] In the present invention, the material B having compressive elasticity is preferred to have heat resistance and cushioning, similarly to the above-mentioned material A having compressive elasticity, and is further preferred to have sealing property. The material B having compressive elasticity may be a non-intumescent material or an intumescent material. The material B having compressive elasticity is preferred to be, for example, a ceramic fiber composed mainly of at least one kind selected from the group consisting of alumina, high alumina, mullite, silicon carbide, silicon nitride, zirconia and titania, or of a composite thereof, and is further preferred to be a mat made of such a fiber. Specifically, there can be used, for example, 1100HT produced by 3M Co. and Maftec produced by Mitsubishi Chemical Corporation, both mentioned above. There can also be used, for example, Interlam Mat produced by 3M Co. (an intumescent mat).

[0031] In the present invention, as the method for accommodating a honeycomb structure 1 and a material B having compressive elasticity in a metallic container 11 in a compressed state, there are suitably used a stuffing method shown in FIG. 3, using a guide 17; a tourniquet method shown in FIG. 4, which comprises winding a metallic plate 11 c round a honeycomb structure, pulling the plate to impart a pressure to the outer surface of the honeycomb structure, and welding and fixing the to-be-jointed areas of the metallic plate 11 c; and a clamshell method shown in FIG. 5, which comprises interposing a honeycomb structure between two metallic container parts 11 a and 11 b with a load being applied to the parts 11 a and 11 b, and welding the to-be-bonded areas (flanges) 16 a and 16 b of the parts 11 a and 11 b to obtain a honeycomb structure/metallic container integrated material. There is also suitably used a method (a swaging method) utilizing metal plastic processing, shown in FIG. 6, which comprises applying a compression force to a metallic container 11 from the outside via a tap (of pressure type) to squeeze the outer diameter of the metallic container 11. There can also be used a method shown in FIG. 7, which comprises squeezing, by plastic processing, the outer surface of a metallic container 11 using a processing jig 18 with the metallic container 11 being rotated, that is, a method which comprises squeezing the outer diameter of a metallic container by rotary forging and thereby imparting a pressure to the outer surface of a honeycomb structure accommodated in the metallic container.

[0032] When the honeycomb structure or honeycomb structure assembly of the present invention is used as a carrier for catalyst in an internal combustion engine, a boiler, a chemical reactor, a fuel cell reformer, or the like, the honeycomb segments used therein are allowed to load thereon a metal having a catalytic activity. As representative metals having a catalytic activity, there are mentioned Pt, Pd, Rh, etc. It is preferred that at least one kind of these is loaded on the honeycomb segments.

[0033] Meanwhile, when the honeycomb structure or honeycomb structure assembly of the present invention is used as a filter for trapping and removing the particulate substance contained in an exhaust gas, for example, as a diesel particulate filter (DPF), it is preferred that the cells of honeycomb structure are plugged alternately at each structure end and the cell walls of honeycomb structure are used as a filter.

[0034] When an exhaust gas containing a particulate substance is taken into a honeycomb structure constituted by honeycomb segments, from its one end, the exhaust gas enters the inside of the honeycomb structure from those holes not plugged at the one end, passes through porous cell walls having a filtration ability, and is discharged from the holes not plugged at the other end. The particulate substance is trapped by the cell walls at the time of its passing through the cell walls.

[0035] As the amount of particulate substance trapped and deposited on cell walls increases, a sudden increase in pressure loss takes place, a load to engine increases, a reduction in fuel efficiency and drivability occurs; hence, the deposited particulate substance is burnt and removed periodically by a heating means such as heater or the like, to regenerate the ability of the filter. In order to promote the combustion during the regeneration, it is possible to load, on the honeycomb structure, the above-mentioned metal having a catalyst activity.

[0036] In the present invention, in order to load a catalyst on a honeycomb structure assembly 8, there can be used a method which comprises holding a honeycomb structure 1 in a metallic container 11 prior to catalyst loading, to form a honeycomb structure assembly 8, and then loading a catalyst on the honeycomb structure 1. According to this method, the risk of chipping-off or breakage of honeycomb structure during catalyst loading can be prevented. It is also preferred that when the honeycomb structure or honeycomb structure assembly of the present invention is used as a catalytic converter, a catalyst component is loaded on a honeycomb segment 2, then a honeycomb structure 1 is formed, and the structure is accommodated and held in a metallic container 11.

[0037] The present invention is described in more detail below by way of Examples. However, the present invention is not restricted to these Examples.

[0038] Incidentally, each of the following honeycomb structures of Examples and Conventional Examples (Comparative Examples) is a filter used for trapping diesel fine particles, which is made of silicon carbide and has a cell wall thickness of 0.38 mm and a cell density of 31 cells/cm² and wherein the passages are plugged alternately at each end of honeycomb structure and the cell walls function as a filter.

EXAMPLE 1

[0039] A silicon carbide powder was used as a raw material. Thereto were added methyl cellulose, hydroxypropoxyl methyl cellulose, a surfactant and water to prepare puddle having plasticity. This puddle was subjected to extrusion molding, and the resulting extrudate was dried using a microwave and hot air. Then, the holes of the dried extrudate were plugged alternately at each end of extrudate with a sealant made of the same material as for the honeycomb structure to be obtained, in such a way that each end of extrudate looked a checkerboard pattern. Then, the resulting material was heated for debindering in a N₂ atmosphere and fired in an Ar atmosphere to obtain honeycomb segments 2(v) which were each ¼ of a column of about 144 mm in diameter and 152 mm in length and accordingly had a fan-shaped section. Four such honeycomb segments 2(v) were bonded into one piece by providing a ceramic fiber-made non-intumescent mat 3 at all the gaps formed by each two close faces of adjacent honeycomb segments 2(v) and using a double sided tape, to obtain a honeycomb structure shown in FIG. 8(a). Round the outer peripheral portion of the honeycomb structure was wound the same ceramic fiber-made non-intumescent mat as mentioned above; the mat-wound honeycomb structure was stuffed in a metallic (SUS 409) container using a tapered jig, to compression-fix the honeycomb structure and the metallic container, whereby a honeycomb structure assembly of 144 mm×152 mm was obtained.

EXAMPLE 2

[0040] Honeycomb segments 2(w), 2(x) and (y) were obtained in the same manner as in Example 1. Twelve rectangular parallelepiped honeycomb segments 2(w) of 30 mm×30 mm×152 mm, four honeycomb segments 2(x) and eight honeycomb segments 2(y) (total twenty four honeycomb segments) were bonded into one piece by providing a ceramic fiber-made non-intumescent mat 3 at all the gaps formed by each two close faces of adjacent honeycomb segments and using a double-coated tape, to obtain a honeycomb structure shown in FIG. 8(b). Round the outer peripheral portion of the honeycomb structure was wound the same ceramic fiber-made non-intumescent mat as mentioned above; the mat-wound honeycomb structure was stuffed in a metallic (SUS 409) container using a tapered jig, to compression-fix the honeycomb structure and the metallic container, whereby a honeycomb structure assembly of 144 mm×152 mm was obtained.

EXAMPLE 3

[0041] Three rectangular parallelepiped honeycomb segments of 30 mm×30 mm×152 mm obtained in the same manner as in Example 1, one honeycomb segment 2(x) and two honeycomb segments 2(y) (total six honeycomb segments) were bonded using an adhesive 7 which was a mixture of colloidal silica, an alumina fiber and water, followed by drying to prepare four honeycomb segments which were each ¼ of a column of about 144 mm in diameter and 152 mm in length and accordingly had a fan-shaped section. These four honeycomb segments were bonded into one piece by providing a ceramic fiber-made non-intumescent mat 3 at all the gaps formed by each two close faces of adjacent honeycomb segments and using a double-coated tape, to obtain a honeycomb structure shown in FIG. 8(c). Round the outer peripheral portion of the honeycomb structure was wound the same ceramic fiber-made non-intumescent mat as mentioned above; the mat-wound honeycomb structure was stuffed in a metallic (SUS 409) container using a tapered jig, to compression-fix the honeycomb structure and the metallic container, whereby a honeycomb structure assembly of 144 mm×152 mm was obtained.

[0042] The effects of the above Examples were evaluated in comparison with the following two conventional samples (Comparative Examples).

COMPARATIVE EXAMPLE 1

[0043] Four honeycomb segments 2(v) obtained in the same manner as in Example 1, which were each ¼ of a column of about 144 mm in diameter and 152 mm in length and accordingly had a fan-shaped section, were bonded into one piece using the above-mentioned adhesive 7 which was a mixture of colloidal silica, an alumina fiber and water, followed by drying to obtain a honeycomb structure of 144 mm (diameter)×152 mm, shown in FIG. 9(a). Round the outer peripheral portion of the honeycomb structure was wound a ceramic fiber-made non-intumescent mat; the mat-wound honeycomb structure was stuffed in a metallic (SUS 409) container using a tapered jig, to compression-fix the honeycomb structure and the metallic container, whereby a honeycomb structure assembly was obtained.

COMPARATIVE EXAMPLE 2

[0044] Twelve rectangular parallelepiped honeycomb segments 2(w) of 30 mm×30 mm×152 mm obtained in the same manner as in Example 1, four honeycomb segments 2(x) and eight honeycomb segments 2(y) (total twenty four honeycomb segments) were bonded into one piece using the above-mentioned adhesive 7, followed by drying to obtain a honeycomb structure of 144 mm (diameter)×152 mm, shown in FIG. 9(b). Round the outer peripheral portion of the honeycomb structure was wound a ceramic fiber-made non-intumescent mat; the mat-wound honeycomb structure was stuffed in a metallic (SUS 409) container using a tapered jig, to compression-fix the honeycomb structure and the metallic container, whereby a honeycomb structure assembly was obtained.

[0045] The thus-obtained honeycomb structure assemblies of Examples 1 to 3 and Comparative Examples 1 to 2 were comparatively evaluated by a hot vibration test. The test conditions were as follows. The vibration acceleration was set at 30 G (30×9.8 m/sec²); the vibration frequency was set at 100 Hz; heating was conducted for 10 minutes using an exhaust gas having an inlet temperature of 800° C. and a flow rate of 2.6 Nm³/min.) and cooling was made for 10 minutes to 100° C. or less using air of ordinary temperature, and this heating and cooling cycle was continued until breakage of honeycomb structure took place or up to 200 hours.

[0046] The test results are shown in FIG. 10. In Comparative Examples 1 and 2 wherein all honeycomb segments were bonded physically using the above-mentioned adhesive, the bonded areas in the vicinity of center of the honeycomb structure caused falling-off and breakage; meanwhile, in each of the honeycomb structure assemblies of Examples 1 to 3 according to the present invention wherein a ceramic fiber-made non-intumescent mat was provided at all or at least part of the gaps formed by each two close faces of adjacent honeycomb segments, no change was seen after 200 hours and high durability and reliability was obtained.

INDUSTRIAL APPLICABILITY

[0047] As described above, the honeycomb structure and honeycomb structure assembly of the present invention used a material A having compressive elasticity, at gaps formed by each two close faces of adjacent honeycomb segments; therefore, they showed good durability to heat and vibration. 

1. A honeycomb structure obtained by bonding, into one piece, a plurality of honeycomb segments each having a large number of passages surrounded by cell walls and extending in the axial direction of the segment, characterized in that a material A having compressive elasticity is provided at least at a portion of the gaps formed by each two faces of adjacent honeycomb segments, close to each other.
 2. A honeycomb structure according to claim 1, characterized in that the material A having compressive elasticity is a ceramic fiber-made mat.
 3. A honeycomb structure according to claim 2, characterized in that the ceramic fiber-made mat is a non-intumescent mat composed mainly of alumina or mullite.
 4. A honeycomb structure according to any of claims 1 to 3, characterized in that the honeycomb structure is used for purification of exhaust gas of automobile.
 5. A honeycomb structure according to any of claims 1 to 4, characterized in that the honeycomb structure is used as a filter for trapping diesel fine particles.
 6. A honeycomb structure according to any of claims 1 to 5, characterized in that the main component of the honeycomb segment comprises at least one kind of ceramic selected from the group consisting of silicon carbide, silicon nitride, cordierite, alumina, mullite, zirconia, zirconium phosphate, aluminum titanate, titania and combinations thereof, a Fe—Cr—Al type metal, a nickel-based metal, or metallic Si and SiC.
 7. A honeycomb structure assembly comprising a metallic container, a honeycomb structure according to any of claims 1 to 6, obtained by bonding, into one piece, a plurality of honeycomb segments each having a large number of passages surrounded by cell walls and extending in the axial direction of the segment, wherein a material A having compressive elasticity is provided at least at a portion of the gaps formed by each two faces of adjacent honeycomb segments, close to each other, and a material B having compressive elasticity, in which honeycomb structure assembly the material B having compressive elasticity is provided on the outer peripheral portion of the honeycomb structure in a compressed state and thereby the honeycomb structure is compression-held in the metallic container.
 8. A honeycomb structure assembly according to claim 7, characterized in that the material B having compressive elasticity is a ceramic fiber-made mat.
 9. A honeycomb structure assembly according to claim 8, characterized in that the ceramic fiber-made mat is a non-intumescent mat composed mainly of alumina or mullite.
 10. A honeycomb structure assembly according to claim 8, characterized in that the ceramic fiber-made mat is a heat-intumescent mat containing vermiculite.
 11. A honeycomb structure assembly according to any of claims 7 to 10, characterized in that the honeycomb structure assembly is obtained by canning by a stuffing method, a tourniquet method, a clamshell method or a swaging method.
 12. A honeycomb structure assembly according to any of claims 7 to 11, characterized in that the honeycomb structure assembly is obtained by loading a catalyst on the honeycomb segments and then accommodating the catalyst-loaded honeycomb segments in the metallic container.
 13. A honeycomb structure assembly according to any of claims 7 to 11, characterized in that the honeycomb structure assembly is obtained by accommodating the honeycomb segments in the metallic container and then loading a catalyst on the honeycomb segments. 